Microstructures of dissimilar friction stir welded joints between 1100 aluminum alloy and AZ31 magnesium alloy

Author(s):

M. Azizieh , A. R. Sadeghi , A. H. Kokabi

Message:
Abstract:
In this study, friction stir welding (FSW) was used for joining AL-1100 to AZ31. In the rotation speed between 400 to 800rpm and travel speed between 15 to 30mm/min, in the condition that stirring pin was inserted in Mg side of weld, friction stir welded samples without any defect were made. In high rotation speed, intermetallic compounds were seen in the XRD results of the stir zone. The best tensile strength, about 122MPa, was reached in rotation speed of 570rpm and travel speed of 20mm/min.
Keywords:

Friction stir welding , Aluminum alloy , Magnesium alloy , Mechanical properties , Microstructure

Language:
Persian
Published:
New Materials, Volume:2 Issue: 2, 2012
Page:
1
magiran.com/p1032961  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
اطلاعات بیشتر
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!
More information