EFFECT OF CALCINATION TEMPERATURE OF THE KAOLIN AND MOLAR Na2O/SiO2 ACTIVATOR RATIO ON PHYSICAL AND MICROSTRUCTURAL PROPERTIES OF METAKAOLIN BASED GEOPOLYMERS
Author(s):
Abstract:
Metakaolinite-based geopolymer has been synthesized at about 25 °C from metakaolin which has been calcined in different temperatures (600-900 °C) and different Na2O/SiO2 ratio activator (0.3-1.1). Compressive strength and microstructure of cement pastes after 7-28 days curing at ambient temperature were measured. Compressive strength tests on the samples showed that the sample made with calcined kaolin at 700 °C and molar ratio of 0.6 has highest average compressive strength of 32 MPa after 28 days of curing. Evaluation of infrared spectroscopy (FTIR) and microstructure showed that geopolymer cement developed and new molecular structure established
Keywords:
Language:
English
Published:
Iranian Journal of Materials science and Engineering, Volume:9 Issue: 4, Dec 2012
Pages:
43 to 51
magiran.com/p1101307
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!