Effect of Temperature on Mechanical and Microstructural Properties of Hydroxyapatite-Alumina/Zirconia Nanocomposites

Message:
Abstract:
Two- step sintering (TSS) has been applied, in the present work, to suppress the accelerated grain growth of Hydroxyapatite Zirconia Alumina nanocomposites in the last sintering stage. The average grain size of near full dense specimens made via conventional sintering (CS) was around 400nm. By using novel tow- step sintering, however, the final grain size (200nm) dropped 2 times less than that for specimens produced by the CS method. After densification, the mechanical properties, the relative proportion of TCP formed and the microstructures of the composite were observed. By used of two step sintering, highest hardness and fracture toughness, lowest relative proportion of TCP and nanostructure were achieved.
Keywords:

Tow , Step Sintering , Mechanical , Microstructural Properties , Hydroxyapatite , Alumina , Zirconia Nanocomposites

Language:
Persian
Published:
Iranian Journal of Ceramic Science & Engineering, Volume:1 Issue: 2, 2013
Page:
29
magiran.com/p1104553  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
اطلاعات بیشتر
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!
More information