Effect of Different Powers of Er,Cr:YSGG Laser Treatment on Surface Morphology of Microhybride Composite Resin: Scanning Electron Microscope (SEM) Evaluation

The aim of this study was to evaluate and compare microhybride composite treated by bur and different power of Erbium, Chromium doped Yttrium Scandium Gallium Garnet (Er,Cr:YSGG) laser by Scanning Electron Microscope (SEM). 21 microhybride composite blocks (DiaFil TM, DiaDent, Korea) with 2 × 4 × 4 mm dimensions were made. The bonding surface of these blocks were polished, The samples were put into 6 groups for laser irradiation as follows: Group 1 (power: 1W, Energy: 50 mJ); Group 2(power: 2 W, Energy: 100mJ); Group 3 (power: 3W, Energy: 150mJ); Group 4 (power: 4W, Energy: 200mJ); Group 5 (power: 5W, Energy: 250mJ) and Group 6(power:6 W, Energy: 300mJ). One group prepared by bur- treated. All samples were prepared by repetition rate of 20 Hz. Then, the samples were prepared for SEM examination. Some irregularities were seen in Er,Cr:YSGG laser samples in comparison to Bur group that produced favorable surface for adhesion of repair composite. Among different lasers, Er;Cr:YSGG laser can be chosen as a suitable technique for surface treatment of unsatisfactory composites.