Experimental study of Manganese oxide nanostructures (MnO2, Mn3O4, Mn2O3) and their magnetic properties

Abstract:
Manganese oxide nanoparticles were synthesized by sol-gel technique. Annealing in 250°C leading to produce Mn3O4 .Mn2O3 was obtained by increasing annealing temperature.Potassium permanganate and maleic acid were used to produce MnO2 at room temperature.The structural properties of manganese oxides were investigated by XRD spectrum and the average crystallite size were identified in the range of 38-51nm.The magnetic properties of the samples were studied by VSM. The effect of annealing temperature on the hysteresis cycle showed different χm for Mn3O4 and Mn2O3.
Keywords:

Manganese oxide nanoparticles , sol-gel , magnetic properties

Language:
Persian
Published:
Iranian Journal of Physics Research (IJPR), Volume:17 Issue: 1, 2017
Pages:
145 to 150
magiran.com/p1682211  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
اطلاعات بیشتر
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!
More information