Effect of Proanthocyanidin, Fluoride and Casein Phosphopeptide Amorphous Calcium Phosphate Remineralizing Agents on Microhardness of Demineralized Dentin

The aim of this study was to evaluate the effect of dentin remineralization using proanthocyanidin (PA), fluoride varnish and casein phosphopeptide amorphous calcium phosphate (CPP-ACP) paste and their various combinations on microhardness of demineralized root dentin.
One-hundred and twenty freshly extracted sound human premolars were selected and randomly divided into eight groups for dentin treatment as follows. C: Deionized water (control); PA: 6.5% PA solution; F: fluoride varnish (5% NaF, 22600 ppm fluoride); CP: CCP-ACP; PAF: 6.5% PA fluoride varnish; PACP: 6.5% PA CCP-ACP; FCP: fluoride varnish CCP-ACP and PAFCP: 6.5% PA fluoride varnish CCP-ACP. All specimens were subjected to Vickers microhardness test (500 g, 10 seconds, 3 points). Data were analyzed using one-way ANOVA and Tukey’s post hoc test. The significance level was set at 0.05.
The mean and standard deviation (SD) values of Vickers hardness number (VHN) in groups C, PA, F, CP, PAF, PACP, FCP and PAFCP were 37.39±4.97, 38.68±4.62, 48.28±2.68 ,41.91±3.32, 48.59±2.55, 53.34±2.57, 48.413±4.00 and 55.20±1.82, respectively. Pairwise comparisons of the groups revealed that there was no significant difference between groups C and PA, PA and CP, F and PAF, F and FCP, PAF and FCP, and PACP and FPACP (P>0.05); but significant differences were observed between other groups (P The results of this study showed that the tested dentin treatments increased the microhardness of demineralized root dentin except for PA application.