The Effect of Fractional CO2 Laser Irradiation on Shear Bond Strength of Resin Cement to Feldspathic Porcelain Untitled

This study investigated the effect of fractional CO2 laser on shear bond strength (SBS) of resin cement to feldspathic porcelain.
Sixty blocks of unglazed feldspathic porcelain were randomly divided into 5 groups of 12 by treatment. Group 1 and 2 underwent etching with 9.6% hydrofluoric acid (HF) and air abrasion with alumina particles, respectively. In groups 3 and 4, a fractional CO2 laser was applied for 10 seconds using 20 W/10 mJ (group 3) or 15 W/20 mJ (group 4). The specimens in group 5 were first treated by fractional CO2 laser (15 W/20 mJ) and then etched by HF acid. After silane application, a resin cement (Clearfil SA) was poured into plastic molds over the porcelain surface and light cured. SBS was assessed by a universal testing machine and the type of bond failure was determined.
Analysis of variance (ANOVA) indicated a significant difference in SBS among the study groups (P The application of fractional CO2 laser followed by HF acid treatment can improve SBS of resin cement to feldspathic porcelain and could be recommended when demanding extra retention.