FCC catalyst attrition behavior at high temperatures
Author(s):
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
In this work, high temperature attrition was studied in a standard attrition set-up to mimic the FCC regenerator environment with mechanical attrition. Operating conditions were modified in this pilot due to the application of high temperatures. Two parameters, i.e., time and temperature in the ranges of 1 to 5h and 673-973K, were surveyed, respectively. The behavior of attrition and mass loss was then modeled and validated. At higher temperatures mass loss response sensitivity became larger. Finally, PSD and SEM tests were used to investigate the attrition mechanism. In the ambient tests, abrasion was significant while at higher temperatures, fragmentation was considerable. PSD plots shifted into larger particles and SEM images showed those changes as well. In addition, significant reshaping in the PSD curves indicated particle cracking at high temperatures.
Keywords:
Language:
English
Published:
Journal of Particle Science and Technology, Volume:5 Issue: 3, Autumn 2019
Pages:
135 to 143
magiran.com/p2195529
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!