The Effect of Zircon on Long-Time Corrosion Resistance of Alumina
Message:
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
Corrosion resistance of zircon reinforced alumina refractories has been carried out through static crucible test. The corrosion measurements with percentage, the penetration depth of molten steel and the microstructure of the refractories were evaluated after soaking 150 h at the temperature of 1500˚C. Results showed that the corrosion resistance of alumina increased by adding 20 wt% zircon, and decreased with further increasing of zircon. Also, the samples containing 20 wt% of zircon obtained the minimum porosity. Microstructural features of this composite showed needle-like mullite grains and higher amount of zirconia particles which may be responsible for providing the corrosion resistance to melt penetration.
Language:
English
Published:
Advanced Ceramics Progress, Volume:3 Issue: 4, Fall 2017
Pages:
41 to 48
magiran.com/p1885553  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
دسترسی سراسری کاربران دانشگاه پیام نور!
اعضای هیئت علمی و دانشجویان دانشگاه پیام نور در سراسر کشور، در صورت ثبت نام با ایمیل دانشگاهی، تا پایان فروردین ماه 1403 به مقالات سایت دسترسی خواهند داشت!
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!