The corrosion behaviour of hydroxyapatite coating on TiO2 nanotubes in SBF solution by electrophoretic deposition

Author(s):

Mona Goodarzi , Abdollah Afshar , Abolghasem Dolati , Iman Pooladvand

Message:
Abstract:
Anodic oxidation can be done in order to obtain a porous structure، and to obtain TiO2 nanotubes. In the current research، first، titanium dioxide nanotubes were fabricated by anodic oxidation and then hydroxyapatite nanoparticles have been deposited onto nanotublar TiO2 by electrophoretic deposition at 30V for 10min and then sintered at 400°С for 2hr. Corrosion behavior in SBF at 37˚С was evaluated. The results show that formation of TiO2 nanotubes and sintering improve corrosion behavior in SBF.
Keywords:

Hydroxyapatite , TiO2 Nanotubes , Electrophoretic , Corrosion , SBF Solution

Language:
Persian
Published:
Iranian Journal of Surface Science and Engineering, Volume:8 Issue: 16, 2013
Page:
1
magiran.com/p1105436  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
اطلاعات بیشتر
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!
More information