Comparative Evaluation of the Reinforcing Effect of Different Post Systems in the Restoration of Endodontically Treated Human Anterior Teeth at Two Different Lengths of Post Space Preparation- An in Vitro Study
Message:
Abstract:
Objectives
Comparative evaluation of the reinforcing effect of different post systems in the restoration of endodontically treated human anterior teeth at two different lengths of post space preparation- an in vitro study
Materials And Methods
135 extracted human incisors were endodontically treated, out of which 120 teeth were decoronated 2mm above the cementoenamel junction and divided into four experimental groups based on the post system to be used: Glass fiber post (GFP) and stainless steel post (SSP), titanium post (TTP), cast metal post (CMP). Each group was divided into two sub-groups according to the length of post space preparation: 5mm and 10mm. All the samples were restored with metal crowns. The fracture resistance was measured by applying loads at an angle of 135º to the long axis of teeth in an instron universal testing machine. Fracture mode was analyzed for all the samples. Results from the four test groups were compared and analysed using one-way ANOVA test and the Post-hoc Bonferroni test to demonstrate differences between pairs of groups.
Results
The results revealed that SSP group at 10mm post space length showed the significantly (“P-value< 0.05”) highest fracture resistance (793.7787 N). Decrease in post length resulted in the decrease in fracture resistance in all the groups reduced to values even lesser than the control (437.8733N).
Conclusion
The different post systems used in the study were able to reinforce endodontically treated teeth only at 10mm post space length.
Language:
English
Published:
Frontiers in Dentistry, Volume:10 Issue: 2, 2013
Page:
124
magiran.com/p1112651  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.