A Comparison of Viscoelastic Properties of Three Root Canal Sealers
Message:
Abstract:
Objective
Handling of endodontic sealers is greatly dependent on their elasticity and flow ability. We compared the viscoelastic properties of three root canal sealers.
Materials And Methods
AH Plus (Dentsply, De Trey, Konstanz, Germany), Endofill (Dentsply Hero, Petrópolis, Rio de Janeiro, Brazil) and AH26 (Dentsply, De Trey, Konstanz, Germany) were mixed according to the manufacturer's instructions. The resulted pastes were placed on the plate of a rheometer (MCR 300, Anton-Paar, Graz, Austria). The experiments were performed at 25˚C and 37˚C. Viscoelastic properties of the sealers including loss modulus (G"), storage modulus (G´) and complex viscosity (η*) were studied using dynamic oscillatory shear tests. The shear module versus frequency (from 0.01 to 100 S-1) curves were gained using frequency deformation sweep test. Three samples of each material were examined at each temperature. The mean of these three measurements were recorded.
Results
The storage modulus of AH plus was higher than its loss modulus at two temperatures. Endofill exhibited a crossover region in which the storage modulus crosses the loss modulus in both temperatures. At 25ºC the loss modulus of AH26 was higher than the storage modulus (G">G¢). In contrast, at 37ºC G¢was greater than G² (G¢>G²). Both shear modules of AH Plus and Endofill decreased as the temperature raised from 25ºC to 37ºC. On the contrary, the loss modulus and storage modulus of AH26 increased at 37ºC.
Conclusion
In both test temperatures, AH Plus behaved like viscoelastic solids and Endofill exhibited a gel-like viscoelastic behavior. AH26 at 25ºC behaved like liquids, while at 37ºC it was an elastic solid-like material.
Language:
English
Published:
Frontiers in Dentistry, Volume:10 Issue: 2, 2013
Page:
147
magiran.com/p1112654  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.