The effect of microwave/laboratory light source postcuring technique and wet‐aging on microhardness of composite resin
Message:
Abstract:
Background
Although composite restorations are really valuable for esthetic zones, they have shown less longevity rather than amalgam restorations. Since it may be related to the method used for curing the composite, postcuring could increase the degree of conversion and result in more long‑lasting composite restorations. This study was planned to evaluate the effect of two different postcuring techniques on microhardness of indirect composite resin after wet‑aging and comparing them with the direct type.
Materials And Methods
In this experimental study, 99 composite disk‑shaped (6.5 × 2.5 mm) specimens of composite (Gradia GC, Japan) were prepared in split mold. The indirect composite specimens were postcured by laboratory light source (Labolite LV‑III GC Corp, Japan) or microwave unit (MC 2002 JR, LG, Korea). Then, the aging procedure was done for 24 h, 30 and 180 days in distilled water. The Vicker’s Hardness test (VHN) on surface of specmens was measured by Wolpert microhardness tester and the data were analyzed by the two‑way analysis of variance (ANOVA) and Tukey’s post hoc tests. (P ≤ 0.05).
Results
The statistical analysis revealed that surface microhardness of postcured composite by microwave and laboratory light source was more than that of direct composite (P = 0.0001) and postcuring by microwave was more effective than postcuring by laboratory light source (P = 0.004). The 30 days stored composite demonstrated significant decrease of VHN compared with the 24‑h stored samples (P = 0.0001), with a more significant VHN decrease after 180 days of aging (P = 0.045).
Conclusion
Postcuring increased the surface microhardness and aging reduced the surface microhardness of indirect composite.
Language:
English
Published:
Dental Research Journal, Volume:10 Issue: 3, 2013
Page:
370
magiran.com/p1168607  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.