Effective of three Methods of curing and load cycling on microleakage of class V resin composite restorations
Message:
Abstract:
Objective
Different methods have been suggested to overcome the polymerization shrinkage of composite restorations. Changing the light curing protocol to improve polymerization by using new light curing units is among these methods. The new devices are more efficient, portable and durable and produce less heat. This study aimed to assess the marginal microleakage of class V composite restorations subjected to three different light curing protocols and mechanical cycles.
Methods
This was an in-vitro experimental study. Class V cavities measuring 2x3x1.5 mm were prepared on the buccal and lingual surfaces of 90 extracted human premolar teeth 1.5 mm above and below the cement enamel junction(CEJ). The samples were selected using convenience sampling and divided into 9 experimental groups of 10 each by using the Table of Random Numbers to control for the bias. The cavities were restored with packable composite resin along with Tetric-N-Bond and cured using three light curing protocols of conventional (680 mW/cm2 for 30s), soft-start (380 mW/cm2 for 10s followed by 680 mW/cm2 for 20s) and pulse (680 mW/cm2 for 30s,1s interval and 1s of lighting). The teeth were then subjected to mechanical cycles of 0, 500,000 and 1,000,000 and immersed in 2% Fuchsin for 24h. The teeth were then sectioned in half from the middle of the restoration buccolingually and the degree of microleakage was evaluated under a stereomicroscope (Zeiss, Germany) with 40X magnification. Data were analyzed using the Kruskal Wallis and the Mann Whitney tests.
Results
Despite the structural differences between the enamel and dentin margins, no significant difference was found in the degree of microleakage between the enamel (occlusal wall, P>0.05) and dentin (gingival wall, P>0.05) margins among the understudy groups.
Conclusion
The degree of marginal microleakage in soft-start (SS) polymerization was not significantly different from that in conventional and pulse polymerizations of class V composite restorations.
Language:
Persian
Published:
Journal of Dental School, Volume:32 Issue: 1, 2014
Pages:
8 - 16
magiran.com/p1259472  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
پرداخت با کارتهای اعتباری بین المللی از طریق PayPal امکانپذیر است.
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.