Fabrication and Characterization of Nano-porous beta-Sialon Ceramic Articles Prepared via Gel-casting
Abstract:
Antenna protection against external factors (e. g. wind، rain، and objects colliding) is done by radome. In addition to acceptable mechanical properties، radome should satisfy suitable electrical properties such as dielectric constant and loss tangent to prevent negative effect on antenna performance. In order to build radome to be utilizing at high temperatures (over 1000 °C)، for flying objects with hypersonic speed (5 to 10 Mach)، engineering ceramics are used. Porosity affects the electrical and mechanical properties of articles. It simultaneously reduces the dielectric constant and flexural strength. In this study porous ceramic articles of beta-Sialon were fabricated by ball milling beta-Sialon powder، monomers and water for 10 hours and under 20 MPa uniaxial pressure. Average porosity size of this sample is 200 nm with 30% of its porosities are below 100 nm. Dielectric constant and loss tangent of this sample with 20% porosity in 8-12 GHz is 5. 3 and 0. 04، respectively.
Language:
Persian
Published:
Iranian Journal of Ceramic Science & Engineering, Volume:3 Issue:3, 2014
Page:
73
magiran.com/p1386517  
روش‌های دسترسی به متن این مطلب
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!