The Influence of Anodising Voltage on Tribocorrosion Behavior of Anodized Ti-6Al-4V Alloy
Message:
Abstract:
In this study، the chemical composition، thickness and tribocorrosion behavior of oxide films prepared on Ti-6Al-4V alloy by anodising treatment in H2SO4/H3PO4 electrolyte at the potentials higher than the dielectric breakdown voltage were evaluated. The thickness measurement of the oxide layers showed a linear increase of thickness by increasing the anodizing voltage. The EDS analysis of oxide films demonstrated precipitation of sulfur and phosphor elements from electrolyte into the oxide layer. Tribocorrosion results indicated that the tribocorrosion behavior of samples was significantly improved by anodising process. Furthermore، the tribocorrosin performance of thesamples anodised at higher voltages was enhanced. SEM and EDS of worn surfaces indicated that the oxide layer on the samples anodised at lower voltages was totally removed، but for the samples anodised at higher voltages، the oxide layer was only locally removed within the wear track. Moreover، measurement of wear volume of the treated samples exhibited lower values on the samples anodised at higher voltages.
Language:
Persian
Published:
Journal of Advanced Materials in Engineering, Volume:33 Issue:3, 2015
Pages:
37 - 49
magiran.com/p1390081  
روش‌های دسترسی به متن این مطلب
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!