Friction reduction during sliding in different angles with Zno nanoparticles deposition on orthodontic wires
Abstract:
Aim: Friction accompanies all sliding techniques. Sliding is in the manner of tipping and uprighting with increasing angle between bracket and wire. Recently, wire coating with the different nanoparticles has been proposed to decrease the frictional forces. The present study was done to coat the stainless steel wires with the ZnO nanoparticles and determine the effect of this coating on friction reduction during different angle between the wires and brackets.
Materials And Methods
Eighty pieces of 0.016 stainless steel wires with and without zinc oxide nanoparticles were used in 80 pieces of orthodontic brackets (0.018). The coated wires analyzed by the SEM and XRD observations. Friction between the wires and orthodontic brackets at 0,5,10 degree angle were calculated using universal testing machine. Two and three group comparisons were done by means of Student t and one-way ANOVA respectively and Tukey post hoc test was used to assess the paired comparisons.
Results
Frictional values were significantly increased with the increased angles between the wire and bracket. the increased friction force from 0 to 10 degree in uncoated wires were Statistically more significant than increased friction force from 0 to 10 degree in coated wires (p
Conclusion
considering the positive effects of zinc oxide nanoparticles coating in decreasing frictional forces, they might offer a novel opportunity to significantly reduce friction during sliding and consequent better anchorage control, reduced risk of root resorption.
Language:
English
Published:
Iranian Journal of Orthodontics, Volume:6 Issue: 1, 2012
Page:
1
magiran.com/p1505600  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.