Electrochemical Deposition Of Ni/TiN Nanocomposite Coating By Direct Current
Abstract:
Nickel coating has a poor surface mechanical properties. In order to improve the mechanical properties, nickel were covered with ceramic particles. In this study, the Ni/TiN composite coatings were produced by Watts bath containing TiN nanoparticles. The effects of deposition current density, electrolyte agitation speed and the number of particles were investigated. The presence of particles was determined by EDS analysis and the coating morphology was examined by SEM. The corrosion samples were examined by linear polarization tests. It was observed that the maximum amount of particles is formed at the current density of 4 A/dm2 and the agitation speed of 450 rpm.
Language:
Persian
Published:
Journal of Metallurgical And Materials Engineering, Volume:27 Issue: 1, 2016
Pages:
11 - 22
magiran.com/p1514235  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.