Effect of Deposition Current Density on Superhydrophobicity Characteristic and Corrosion Resistance of Nickel Electrodeposited Coating
Message:
Abstract:
The purpose of this work is to investigate the effect of deposition current density on superhydrophobicity characteristic and corrosion resistance of nickel electrodeposited coating. Nickel coating with hierarchical structure was fabricated on copper substrate by electrodeposition process at current density of (10 and 20) mA/cm2. The surface morphology of electrodeposited nickel coatings was examined by scanning electron microscope which showed that the coating structure consisted of micro and nano shaped cones and the size of micro cones decreased by increasing the current density. The relative texture of the coatings was also determined by X-ray diffraction pattern. The results showed that the relative texture direction changed from (220) to (311) by increasing the current density from 10 to 20 mA/cm2. The surface topography studies by atomic force microscope showed decrease in surface roughness by increasing the current density. The wet angle measurement results showed that the wettability of nickel coatings varied from super- hydrophilicity to super- hydrophobicity by exposing the coating in air at room temperature. The reason of this behavior is the formation of NiO on the surface of rough nickel film which decreased the surface energy. The corrosion behavior of the coatings was evaluated in 3.5wt% NaCl solution by electrochemical impedance spectroscopy and potentiodynamic polarization tests. Results revealed the positive effect of hydrophobicity on increase in corrosion resistance of coatings and it was shown that the coating formed at 20 mA/cm2 had higher polarization resistance compared to other coating.
Language:
Persian
Published:
Iranian Journal of Surface Science and Engineering, Volume:12 Issue: 27, 2016
Pages:
1 - 15
magiran.com/p1548830  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 700,000ريال می‌توانید 100 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.