Shear Bond Strength of a Resin Cement to Different Alloys Subjected to Various Surface Treatments

Micromechanical retention of resin cements to alloys is an important factor affecting the longevity of metal base restorations. This study aimed to compare the bond strength and etching pattern of a newly introduced experimental etchant gel namely Nano Met Etch with those of conventional surface treatment techniques for nickel-chrome (Ni-Cr) and high noble alloys.
A total of 120 discs (8×10×15 mm) were cast with Ni-Cr (n=20), high noble BegoStar (n=50) and gold coin alloys (n=50). Their Surfaces were ground with abrasive papers. Ni-Cr specimens received sandblasting and etching. High noble alloy specimens (begoStar and gold coin) received sandblasting, sandblasting-alloy primer, etching, etch-alloy primer and alloy primer alone. Cylindrical specimens of Panavia were bonded to surfaces using Tygon tubes. Specimens were subjected to micro-shear bond strength testing after storing at 37°C for 24 hours.
In gold coin group, the highest bond strength was achieved after sandblasting (25.82±1.37MPa, P For the Ni-Cr alloy, etching was more efficient than sandblasting but for the high noble alloys, higher Au content increased the efficacy of etching.