Compressive Strength of Mineral Trioxide Aggregate with Propylene Glycol

The aim of this study was to evaluate the effect of adding propylene glycol (PG) to mineral trioxide aggregate (MTA) liquid with volume ratio of 20% on the compressive strength (CS) of MTA in two time periods (4 and 21 days) after mixing.
Methods and Materials: Four groups of steel cylinders (n=15) with an internal diameter of 3 and a height of 6 mm were prepared and MTA (groups 1 and 2) and MTA (80% MTA liquid% PG) (groups 3 and 4) were placed in to the cylinders. In groups 1 and 3 the CS was evaluated after 4 days and in groups 2 and 4 after 21 days. Data were calculated using the two-ways ANOVA. The level of significance was set at 0.05.
The highest (52.22±18.92 MPa) and lowest (4.5±0.67 MPa) of CS was obtained in 21-day MTA samples and 4-day MTA specimen, respectively. The effect of time and PG were significant on the CS (P Considering the limitations of this study, PG had a negative effect on CS of MTA.