In Vitro Microleakage of Class V Composite Restorations in Use of Three Adhesive Systems
Abstract:
Background And Aim
Microleakage is a drawback of composite restorations and it is more noticeable in dentinal walls. Despite advances in dentin bonding agents, no adhesive can completely eliminate microleakage and provide a hermetic seal. This study aimed to compare microleakage of three resin bonding agents namely a universal adhesive, two-step self-etch system and two-step total-etch system.
Materials And Methods
This in vitro, experimental study was conducted on 68 human molars. Class V cavities were prepared in the buccal or lingual surfaces of the teeth with occlusal margins in the enamel and gingival margins in dentin. The teeth were then randomly divided into four groups of 17. Group A: Adper Single Bond 2, group B: Clearfil SE Bond, group C: Scotchbond Universal adhesive (self-etch) and group D: Scotchbond Universal adhesive (total-etch). The teeth were then restored using different bonding agents and a microhybrid composite resin. The specimens were then subjected to 1000 thermal cycles between 5-55°C. The entire restoration surface except for 1mm around the margins was coated with nail varnish. The teeth were immersed in 2% methylene blue for 24 hours and sectioned longitudinally in a buccolingual direction and observed under a stereomicroscope to determine microleakage. Microleakage in use of the three bonding agents was compared using the Kruskal Wallis test (P
Results
Based on the Kruskal Wallis test, no significant difference was noted in enamel and dentin margins among different adhesives but the enamel margin showed less microleakage than the dentin margin.
Conclusion
Different adhesive systems tested in this study showed similar microleakage at the enamel and dentinal margins.
Language:
English
Published:
Journal of Islamic Dental Association of IRAN, Volume:28 Issue: 1, 2016
Pages:
14 - 19
magiran.com/p1710344  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.