Effect of delayed light curing methods on push-out bond strength of glass fiber posts in different root canal regions

Delay in light irradiance can improve the polymeric structure and mechanical properties of resin cement and uniform stress distribution. The aim of this study was to evaluate the effect of light activation modes (immediate, 5 and 10-minute delay) on the push-out bond strength of cemented fiber posts with two types of resin cements in different of root canal regions.
In sixty extractedsingle canal and endodontic therapied roots, FRC Postec Plus were cemented with two resin cements, Nexus3 and Panavia F2.0, in three curing methods, immediate, 5, and 10 minute delay. After 24 hours storing in a dark place, they were cut into three sections: coronal, middle and apical. The push-out bond strength test was performed using the universal testing machine. Failure modes were evaluated using stereomicroscope. Data were analyzed by ANOVA and Tukey post hoc test with P In Nexus3, the immediate light curing had significantly higher bond strength (11.18±4.32) than delay methods (P=0.001). In Panavia F2.0, the 5-minute delay had significantly the highest bond strength (13.34±4.62) (P0.05).
Delay in light curing of dual-cure resin cement's had different effects on the push-out bond strength.