Characterization of Ni0.5Zn0.5Fe2O4 Ferrite Synthesized by Solution Combustion method in the Presence of Urea and Glycine as fuels
Ni0.5Zn0.5Fe2O4ferrite, was produced by solution combustion synthesis method. In this way, by heating a solution containing an oxidizer and fuel, highly exothermic reaction occurs that results in the production of powder products with the desired compound. Powders produced in three various ratios of the fuel and oxidizer and 1 different modes of fuels (urea, glycine and combinations of these two fuels) were prepared and compared with each other. The maximum combustion temperature occurred in a sample of F/O=1. Based on the results of the XRD analysis, in all samples, spinel ferrite phase crystallized. FESEM photos shows that the type and amount of fuel has a significant impact on morphology and porosity of produced spinel ferrite. According to magnetic measurements, maximum saturation magnetization were obtained in F/O=1.4 and urea which were 67.22 emu/g. Also, all samples have narrow hysteresis loops, which indicates their soft magnetic properties.
Iranian Journal of Ceramic Science & Engineering, Volume:6 Issue:1, 2017
97 - 113  
روش‌های دسترسی به متن این مطلب
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!