Effect of Various Laser Surface Treatments on Repair Shear Bond Strength of Aged Silorane-Based Composite

Successful repair of composite restorations depends on a strong bond between the old composite and the repair composite. This study sought to assess the repair shear bond strength of aged silorane-based composite following surface treatment with Nd:YAG, Er,Cr:YSGG and CO2 lasers.
Seventy-six Filtek silorane composite cylinders were fabricated and aged by 2 months of water storage at 37°C. The samples were randomly divided into 4 groups (n = 19) of no surface treatment (group 1) and surface treatment with Er,Cr:YSGG (group 2), Nd:YAG (group 3) and CO2 (group 4) lasers. The repair composite was applied and the shear bond strength was measured. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey post-hoc test. Prior to the application of the repair composite, 2 samples were randomly selected from each group and topographic changes on their surfaces following laser irradiation were studied using a scanning electron microscope (SEM). Seventeen other samples were also fabricated for assessment of cohesive strength of composite.
The highest and the lowest mean bond strength values were 8.99 MPa and 6.69 MPa for Er,Cr:YSGG and control groups, respectively. The difference in the repair bond strength was statistically significant between the Er,Cr:YSGG and other groups. Bond strength of the control, Nd:YAG and CO2 groups was not significantly different. The SEM micrographs revealed variable degrees of ablation and surface roughness in laser-treated groups.
Surface treatment with Er,Cr:YSGG laser significantly increase the repair bond strength of aged silorane-based composite resin.