Investigation of two step sintering on microstructure and compresive strenght of nano structured forsterite scaffold using lost foam
Author(s):
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
This paper reports the successful synthesis of nano structured forsterite (Mg2SiO4)scaffold with high compressive strength for tissue engineering application. Forsterite slurry was prepared and pre-cut foams were immersed in the slurry for 5 min. The saturated foams were then annealed at various times and temperatures using the two step sintering method. The compressive strength and porosity of the scaffolds were in the range of 0.03-24.16 MPa and 58-88% depends on the heat treatment process, respectively. The J samples consisted of grains in the range of24 to35 nm and micron size pores that could be detected by SEM observation.
Keywords:
Language:
Persian
Published:
New Materials, Volume:7 Issue: 4, 2017
Pages:
125 to 134
magiran.com/p1770847
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!