Fracture Mechanism of CoCrMo Porous Nano-composite Prepared by Powder Metallurgy Route Article in Press
Abstract:
The main aim of this research was to find the mechanism for the failure of the CoCrMo porous nano-composite by characterizing microstructural changes and fractured surface after compression test. For this purpose, porous nano-composites were prepared with the addition of bioactive glass nano-powder to Co-base alloy with 22.5% porosity by the combination of space-holder and powder metallurgy techniques. The micrographs of samples showed that porous nano-composites had the micro and macro pores including open and closed pores. The observed fracture surface in the triple conjunction of sintered powders indicated a complex of intergranular and transgranular fracture mechanisms. The brittle carbide phase related to the higher solute content (Cr and Mo) precipitated at grain boundaries, leading to the intergranular fracture mechanism and transgranular mechanism that was due to the phase transformation during compression test.
Language:
English
Published:
International Journal of Engineering, Volume:31 Issue: 1, 2018
Pages:
19 - 24
magiran.com/p1784940  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.