Study the Physical Properties of Ceramic Tile by Adding Dolomite and Magnesite as Refractory Materials to Engobe Compound
Message:
Abstract:
Water absorption measurement is one of the factors for evaluation of constructional ceramics. The tile components are glaze, engobe and biscuit. The engobe makes a flat surface on ceramic which improves glaze quality and beauty. Water absorption decreases beauty of ceramic and it may separate glaze from the biscuit. The amount of porosity in the structure of the engobe and biscuit affect water absorption. Holes and capillaries increase probability of water movement from the biscuit to the ceramic tile’s surface. Thus changing the engobe components is a way for controlling water movement to the surface. In recent study, the effects of addition of two kinds of refractory materials such as magnesite (MgCO3) and dolomite (CaMg(CO3)2) on water absorption property of ceramic were studied. After sample preparation, engobe and glaze were coated on the biscuit and the ceramic was heated in the furnace at 1134˚C for 42 minutes. Samples were evaluated by X-ray diffraction (XRD), scanning electron microscope (SEM), flexural strength, shrinkage and water absorption methods. The colorimetric measurements for ceramic tile surface were carried out using CIE-L*a*b* standard. The results show that after addition of magnesite and dolomite to the engobe, water absorption decreased. Also, a high shrinkage is carried out for the samples and the flexural strength increases while the brightness (L*) decreases. The SEM micrographs show that after addition of these materials, the particles in the engobe layer are sintered and block the capillaries. Thus they can prevent water diffusion to the glaze surface.
Article Type:
Research/Original Article
Language:
Persian
Published:
Journal of Color Science and Technology, Volume:12 Issue: 1, 2018
Pages:
13 - 21
magiran.com/p1838761  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
پرداخت با کارتهای اعتباری بین المللی از طریق PayPal امکانپذیر است.
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.