Investigation of Microstructure, and Dry Sliding Wear of Hardfaced Layers Produced by FCAW Using Cored Wire Fe-B-C-Ti Alloy
Message:
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
In this study, the microstructure, hardness, and dry sliding wear behavior of the hardfaced layers made by a cored wire Fe-B-C-Ti alloy were investigated. St37 steel was used as the substrate and the deposition of the hardfaced layers was conducted by the flux cored arc welding (FCAW) process under single-, two-, and three-pass conditions. Dry sliding wear tests were performed by a pin-on-disk apparatus, based on ASTM-G99, at room temperature (250C) at the normal applied loads of 50, 100, and 150 N with a constant speed of 0.08 m/s for a sliding distance of 1000 m. The microstructural and phase analyses were carried out by field emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD), respectively. The results showed that the hardfaced layer produced by the single-pass process contains TiC rectangular phase distributed within a matrix containing ferrite and the eutectic of (α-Fe2B). But, the hardfaced layers produced by the two- and three-pass process contain TiB2 hexagonal phase in addition to TiC, which prevents the formation of detrimental FeB phase around Fe2B and reduces the number of micro-cracks. Moreover, the sample hardfaced by the three-pass process had the best wear resistance due to the greater hardness resulted from the higher amounts of TiC and TiB2 phases. In addition, increasing the number of passes has led to the reduction of wear rate at all the three applied loads. At the applied load of 100 N, the wear mechanism for the all three hardfaced samples was an oxidation wear. However, at the applied load of 150 N, the wear mechanism was a combination of oxidation and delamination.
Language:
English
Published:
Iranian Journal of Materials science and Engineering, Volume:15 Issue: 4, Dec 2018
Pages:
19 to 32
magiran.com/p1908807  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
دسترسی سراسری کاربران دانشگاه پیام نور!
اعضای هیئت علمی و دانشجویان دانشگاه پیام نور در سراسر کشور، در صورت ثبت نام با ایمیل دانشگاهی، تا پایان فروردین ماه 1403 به مقالات سایت دسترسی خواهند داشت!
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!