EBSD characterization of nano/ultrafine structured Al/Brass composite produced by severe plastic deformation
Message:
Abstract:
In the present work, nano/ultrafine structured Al/Brass composite was produced by accumulative roll bonding (ARB) up to eight cycles. The evolution of grain refinement and deformation texture and their effect on the mechanical properties were investigated. It was observed that by increasing the ARB cycles, due to the difference in flow properties of the metal constituents, brass layers necked, fractured and distributed in aluminum matrix. After eight cycles, a composite was produced with almost homogeneous distribution of brass fragments in aluminum matrix. Microstructural characterization by electron backscatter diffraction (EBSD) revealed the formation of bimodal structure consisting of equiaxied grains with an average size of ~120 nm and elongated grains after eight cycles, which was attributed to the occurrence of redundant shear and recrystallization. The crystallographic texture results indicated that the major texture components in the aluminum matrix were Brass {011}, S {123}, Goss {011} and Rotated Goss {011}. Moreover, it was concluded that Goss {011} and Rotated Goss {011} components appeared for high number of ARB cycles due to the adiabatic heat during ARB processing. The tensile strength of Al/Brass composite reached 330 MPa, which was 4.23 times and 1.83 times higher than those of annealed aluminum and monolithic aluminum, respectively. Finally, fracture surfaces of samples were studied, using field emission scanning electron microscope (FESEM), to reveal the failure mechanism.
Article Type:
Research/Original Article
Language:
English
Published:
Journal of Ultrafine Grained and Nanostructured Materials, Volume:51 Issue: 2, 2018
Pages:
123 - 138
magiran.com/p1909884  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.