Optimization of micro hardness of nanostructure Cu-Cr-Zr alloys prepared by the mechanical alloying using artificial neural networks and genetic algorithm
Message:
Abstract:
Cu–Cr-Zr alloys had wide applications in engineering applications such as electrical and welding industrial especially for their high strength, high electrical as well as acceptable thermal conductivities and melting points. It was possible to prepare the nano-structure of these age hardenable alloys using mechanical alloying method as a cheap and mass production technique to prepare the non-equilibrium materials such as solid solution structures. In this study, artificial neural networks (ANNs) program was developed to establish the relationship between the practical parameters of mechanical alloying, i.e., weight percentages of Cr and Zr as alloying element, milling times, milling speed, sintering time and temperature, on the micro hardness of prepared Cu-Cr-Zr nanostructure alloys. The results of sensitivity analysis showed that the alloying elements and sintering temperature had the highest and lowest effect on the micro hardness of products, respectively. Also, the optimum milling speed and sintering temperature proposed as 255-291 rpm and 530-590°C, respectively. The established models of ANN introduced to genetic algorithm (GA) for determination of the optimal condition. The results were evaluated using the confirmation experiments. Moreover, the optimal condition of nanostructures alloy preparation with the highest micro hardness had been proposed as 310 Hv with the root mean square error (RMSE) of lower than 3.4%.
Article Type:
Research/Original Article
Language:
English
Published:
Journal of Ultrafine Grained and Nanostructured Materials, Volume:51 Issue: 2, 2018
Pages:
183 - 192
magiran.com/p1909891  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.