Preparation and Characterization of Thermally Stable Nanofiber Based on Polyamide 66/ Poly (amide-imide) Blend
Message:
Abstract:
Using aliphatic polyamides in electrospinning is very interesting due to their unique properties such as processability. But these polymers have some disadvantages of low dimensional stability and poor thermal stability that limited their use. To solve this problem, various methods such as polymer blending have been suggested. In this research, for the first time, a newly synthesized poly (amide-imide) (PAI) polymer was added to polyamide 66 (PA66) and nanofibers fabricated from PA66/PAI blend with different amounts of PAI polymer. Morphology, dynamical-mechanical properties and thermal stability of nanofibers were analyzed by SEM, DMTA, and TGA, respectively. SEM images revealed that the PA66/PAI nanofibers with uniform structure and without beads were prepared even for nanofibers containing 50% PAI. Moreover, with increasing PAI polymer content in PA66/PAI solution, the average nanofiber diameter increased from 319±66 nm for neat PA66 to 522±65 nm for nanofibers containing 50% PAI polymer. DMA results showed that the storage modulus of PA66/PAI nanofibers in both glassy and rubbery regions were higher than that of neat PA66 nanofibers. At 60 °C, the storage modulus values for neat PA66 nanofibers and PA66/PAI containing 50% PAI were 16.85 MPa and 70 MPa, respectively, showing about four times increase. Furthermore, by incorporating PAI polymer into PA66 matrix, glass transition temperature was moved to higher temperatures. TGA data indicated that with increasing the content of PAI polymer, thermal stability of PA66/PAI nanofibers improved significantly; 65 °C increase in Tmax was obtained for nanofibers containing 50% PAI as compared to neat PA66 nanofibers.
Article Type:
Research/Original Article
Language:
Persian
Published:
Advanced Materials Materials and Novel Coatings, Volume:7 Issue: 26, 2018
Pages:
1827 - 1835
magiran.com/p1942320  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.