An investigation on the effect of light cure and self cure composite resins on bonding strength of light cure glass ionomer to dentin (In-vitro)

Author(s):
Abstract:
Statement of Problem: Composite reins have recently become popular for posterior teeth restorations. Gap formation and subsequent microleakage are of the complications resulting from such restorations. One of the techniques to overcome polymerization shrinkage of composite resins is sandwich technique (application of glass ionomer as a base beneath the composite resin). Since polymerization patterns in two types of composite resins (light cure and self cure) differ from each other, various effects on the bond strength between glass ionomer and dentin are expected.
Purpose
The aim of this in vitro study was to evaluate the effects of self- cure and light- cure composite resins in sandwich technique on the bond strength of light cure glass ionomer and dentin.
Materials And Methods
40 extracted human premolars were selected and divided into four groups:Group 1: Light cure glass ionomer of 1mm thickness was placed on dentin.Group 2: 1mm thickness of light cure glass ionomer plus a mass of self cure composite resin of 2mm thickness were placed.Group 3: 1mm thickness of light cure glass ionomer plus light cure composite resin as two separate 1mm layer were placed.Group 4: 1mm thickness of light cure glass ionomer with 37% phosphoric acid etching followed by two separate layers of light cure composite resin of 1 mm thickness were placed.SEM was used to determine gap size ai Gl- dentin and Gi- composite interlaces. The findings were analyzed by ANOVA and t-student tests.
Results
Groups 1 and 2 showed no gap at Gl-dentm interface and also cracks were not observed in all these specimens. In group 3, there was gap between light cure GI and light cure composite resin and cracks were seen in GI, too. Group 4 showed gap at both interfaces and more cracks were seen in GI. Groups I and 2 showed the least gap formation and group 4 showed the most. Statistically significant difference was found between groups 3, 4 and group 1 (control), 2.
Conclusion
Base on this study, the application of self-cure composite resin on light cure GI showed no gap and crack formation on Gl-dentin and Gl-composite interfaces and GI itself. However, light cure composite resins and glass ionomer etching aggregated crack and gap formation.
Language:
Persian
Published:
Journal of Dental Medicine, Volume:16 Issue: 4, 2004
Page:
5
magiran.com/p195918  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 1,390,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!