The Effect of Low Temperature Austempering on Microstructure, Mechanical and Wear Properties of AISI 52100 Steel
Author(s):
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
The goal of this study was to develop nano/ultrafine bainitic microstructure in AISI 52100 steel. For this purpose, the specimens were austenitized, followed by austempering treatment at different temperatures and times. Austempered samples were characterized using field emission scanning electron microscopy, X-ray diffraction and tension and wear tests. The results showed, at austempering temperature up to 250oC, the strength and ductility reached 2000 MPa and 7%, respectively. By further increasing the austempering temperature, the strength and ductility were simultaneously reduced (to about 1808MPa and 3%).
Keywords:
Language:
Persian
Published:
Journal of Metallurgical And Materials Engineering, Volume:30 Issue: 1, 2019
Pages:
13 to 28
magiran.com/p1971535
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
دسترسی سراسری کاربران دانشگاه پیام نور!
اعضای هیئت علمی و دانشجویان دانشگاه پیام نور در سراسر کشور، در صورت ثبت نام با ایمیل دانشگاهی، تا پایان فروردین ماه 1403 به مقالات سایت دسترسی خواهند داشت!
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!