Cathodic Electrodeposition and Characterization of YAG Nanostructure: Effect Current Density on the Morphology
Message:
Abstract:
Abstract YAG (Yttrium Aluminum Garnet) was successfully prepared through cathodic electrodeposition process using applying different current densities to the mixture of YCl3 and AlCl3 dissolved in water/ethanol 1:1 solution. Hydroxide precursors were cathodically grown on the cathode surface (at different current densities) and then the obtained hydroxide powder was heat-treated at 1100 °C for 4 h. The oxide products were characterized by XRD, FTIR, DSC-TGA, SEM and EDAX techniques. The effect of applied current density on the morphology and particle size of YAG nanostructures were investigated through SEM images. Results showed that the cathodic electrodeposition followed by heat-treatment can be used as a facile method for preparation of YAG nanostructures with different morphologies.
Article Type:
Research/Original Article
Language:
English
Published:
Advanced Ceramics Progress, Volume:4 Issue: 2, 2018
Pages:
32 - 36
magiran.com/p2011673  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.