Investigating the Effect of Ultrasonification Time on Transition from Monolithic Porous Network to Size-Tunable Monodispersed Silica Nanospheres via Stöber Method
Message:
Abstract:
Abstract Uniform colloidal monodispersed silica nanoparticles were synthesized via stöber method using ammonia as a basic catalyst. Field Emission Scanning Electron Microscope (FESEM) was confirmed the homogeneous nanospheres. The decrease of TEOS concentration (0.067 to 0.012 mol L-1) and an increase of H2O concentration (3 to 14 mol L-1) at 14 mol L-1 NH3 fixed accelerated the rate of hydrolysis and condensation of [Si (OC2H5)4-X(OH)X]. Using EtOH solvent prevented the aggregation of micelle nuclei and formed spheres with the smallest variance in their size. Hence, the spherical particles were tuned in the range of 10-330 nm. Moreover, the decrement of the ultrasonic time could be changed the nanospheres morphology to the mesoporous structure.
Article Type:
Research/Original Article
Language:
English
Published:
Advanced Ceramics Progress, Volume:4 Issue: 2, 2018
Pages:
37 - 43
magiran.com/p2011674  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
پرداخت با کارتهای اعتباری بین المللی از طریق PayPal امکانپذیر است.
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.