Evaluation of the water absorption content effect on the dielectric properties and tensile strength of polymer composites
Message:
Abstract:
Water absorption tests were performed on unidirectional glass/polymer composite materials used in high voltage composite (nonceramic) insulators. The composites were based on E-glass fibers with polyester resin. The composites were exposed to distilled water at room temperature and their resistance to moisture absorption in terms of the rate of moisture absorption, maximum moisture content and apparent diffusivity was determined. In particular, the effects of specimen geometry (the edge effect) on moisture absorption by the composites were evaluated. It was found that changes in moisture content have a special effect on the mechanical and electrical properties of the composite material. The tensile test was conducted to determine the mechanical properties, breakdown voltage and the leakage current were measured to determine the electrical properties and scanning electron microscopy was used to observe the morphological property of Glass Fiber Reinforced Polymer (GFRP) samples. A reduction in both module and tensile strength was observed with water aging. Furthermore, Water absorbed by composite samples had a detrimental influence on the breakdown voltage and leakage current of composite specimens that could be an indicator of degradation.
Article Type:
Research/Original Article
Language:
Persian
Published:
Journal of Science and Technology Composite, Volume:6 Issue:2, 2019
Pages:
300 - 309
magiran.com/p2019634  
روش‌های دسترسی به متن این مطلب
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!