Effect of bath pH on microstructure and corrosion behavior of manganese phosphate coating on SCM420H steel
Message:
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:

In order to improve the surface quality and prevention of corrosion and reduction of wear in the components like gears and bearings, they can be covered with phosphate coatings. SCM420H alloy steel was coated with manganese phosphate deposition. The microstructure and corrosion resistance of the coating was studied by change of bath pH. In order to investigate the phase analysis and coating microstructure, X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used, respectively. XRD analysis from the coated surface revealed the phases of MnFe2(PO4)2(OH)2H2O, Mn(PO)3، Fe(PO)3 and (Mn,Fe)5H2(PO4)4•4H2O. Results showed the obtained coating at pH=2.1 was uniform and continuous and no crack or porosity observed. The phosphate surface at pH=1.9 and pH=2.4 was non-uniform and included cracks. In order to investigate the corrosion resistance, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) tests were applied on coated and uncoated specimens in 3.5% NaCl solution. The results of potentiodynamic polarization and electrochemical impedance spectroscopy tests were in agree with microscopic images. The results of electrochemical impedance spectroscopy demonostrated that the formed manganese phosphate deposition in bath with pH=2.1 had the highest polarization resistance (28020 Ω) compared to the formed coating in bath at pH=1.9 (1480 Ω) and the formed coating in a bath with pH=2.4 (3155 Ω).

Language:
English
Published:
Journal of advanced materials and processing, Volume:7 Issue: 2, Spring 2019
Pages:
57 - 66
magiran.com/p2045815  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 700,000ريال می‌توانید 100 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.