Synthesis, characterization and application of graphene oxide, graphene oxide quantum dots and graphene quantum dots in photoelectrochemical sensors
Article Type:
Research/Original Article (دارای رتبه معتبر)

In this study, graphene oxide (GO), graphene oxide quantum dots (GOQD) and graphene quantum dots (GQD) were synthesized by Hummers, hydrothermal and the calcination in argon methods, respectively. Then the structure of the samples was characterized by X-ray diffraction, Fourier-transform infrared and Raman spectroscopies and their particle size distribution were investigated by dynamic light scattering. Afterward, the electrical and photoelectric properties of the samples were studied by electrical conductivity meter and diffuse reflectance and photoluminescence spectroscopies. Finally, the photoelectrochemical sensors were designed to detect dopamine (DA) based on GO, GOQD and GQD modified glassy carbon electrodes (GCE). The results showed that the sample of GO has graphene plates with widest particle size distribution (about 1.3 to 5.7 µm) and the highest electrical conductivity (287.9 µS/cm). On the other, the sample of GQD has narrowest particle size distribution (about 5.3 to 12.8 nm) and the lowest electrical conductivity (165.1 µS/cm). The samples of GOQD and GQD have light absorption throughout the range of visible wavelength and therefore have photoelectric behavior better than GO. As a result, in DA detection sensors, the photoresponse of the GCEs modified with GOQD and GQD is 4 times higher than that of GO modified GCE.

Journal of advanced materials and processing, Volume:7 Issue: 2, Spring 2019
64 - 73  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 700,000ريال می‌توانید 100 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.