Effect of nano gel wollastonite on physical, mechanical and morphological properties of bagasse-cement composites
Message:
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:

In this study, the effect of nano gel wollastonite on physical, mechanical and morphological properties of composites made of bagasse and cement has been investigated. The mixing ratio of bagasse as lignocellulosic material with Portland cement at three levels (15:85, 25: 75 and 35: 65%) and nano-wollastonite at three levels of 0, 3 and 7% were considered as the variables of this study. The cake density of all boards were 1.1 g / cm3 and calcium chloride booster 5% for all treatments were considered as constant factors. Mechanical and physical properties of the specimens include modulus of rupture, modulus of elasticity, internal bonding, thickness swelling after 2 and 24 soaking hours in water and density of boards according to DIN-EN-634 and fire resistance (weight loss percentage) according to standard ISO-11925 were measured. In this study, the hydration temperature of a mixture of cement, bagasse and nano-wollastonite was measured using a thermocouple and flux. Also, microscopic images (SEM) of samples were prepared to investigate the morphological properties of composites and their distribution. The results showed that by increasing the amount of nano-wollastonite, the percentage of weight loss boards decreased, the heat of hydration and the physical and mechanical properties improved. The modulus of rupture, modulus of elasticity, and internal bonding of boards decreased with increasing bagasse content and the maximum value was obtained using 15% bagasse. The results also showed that with increasing bagasse content in boards, there was a significant increase in thickness swelling of boards. Inference from microscopic imaging (SEM) showed that the optimum level of nano-wollastonite can fill the empty holes and create a uniform structure and thus improve the properties of the boards.

Language:
Persian
Published:
Iranian Journal of Wood and Paper Science Research, Volume:34 Issue: 3, 2019
Pages:
397 to 408
magiran.com/p2057899  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
دسترسی سراسری کاربران دانشگاه پیام نور!
اعضای هیئت علمی و دانشجویان دانشگاه پیام نور در سراسر کشور، در صورت ثبت نام با ایمیل دانشگاهی، تا پایان فروردین ماه 1403 به مقالات سایت دسترسی خواهند داشت!
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!