Study of Optical Properties, Thermal Kinetic Decomposition and Stability of Coated PETN-Litholrubine nano-Composite via Solvent/None-Solvent Method Using Taguchi Experimental Design
Message:
Abstract:
In this research, in order to coating PETN particles, nano-pigment of redlitholrubine B 57:1 (NLR) was used in a surfactant environment of cetyltrimethylammonium bromide (CTAB) using solvent/none-solvent (water-acetone) method. Afterstructural studies of PETN-NLR nanocomposite by infrared (FT-IR) and field emissionscanning electron microscopy-Energy dispersive X-ray (FESEM-EDX) methods,Taguchi statistical design method was used to investigation and optimization of lightreflectance of nanocomposite at 532 nm. The effect of four factors of NLRconcentration, solvent flow rate, surfactant type and surfactant concentration in threelevels on light reflection was investigated and analysis of variance (ANOVA) showedthat NLR concentration with the participation of 67.24 percent had highest effect.Optimal conditions to achieve a minimum light reflectance were obtained of NLR 5wt%, solvent flow rate 1 mLmin-1, surfactant of CTAB and surfactant concentration1×10-3molLit-1. The lowest light reflectance by analyzing the data variance for optimumconditions was estimated 4.67 ± 2.14%. Also the mean experimental result for lightreflectance of the nanocomposite under optimum conditions was obtained 5.54 percent.Follows, thermal behavior and vacuum stability of the optimal sample was investigatedthat the results, due to the no significance difference in the melting point and thethermal decomposition mechanism of the nanocomposite compared to pure PETN,indicating the compatibility of NLR and CTAB with PETN
Article Type:
Research/Original Article
Language:
English
Published:
Journal of Optoelectronical Nanostructures, Volume:4 Issue: 4, 2019
Pages:
81 - 98
magiran.com/p2057984  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.