Antibacterial activity of CuO - cellulose nano rods depends on anew green synthesis (cotton)
Message:
Abstract:
In this study CuO nano sheets were prepared using the cellulose extracted from green synthesis (cotton) as a novel me project. Structural properties were examined using X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM), and Ultra Violet (UV-Vis). The optimum copper oxide peak was at 2 theta 〖35.44〗^°corresponding to (1 ̅11) while for the cellulose was 〖22.8〗^°corresponds to (002). FESEM images of CuO nano sheets were relatively homogenous with diameters less than 30 nm. The UV-Vis for CuO-cellulose nano rods was observed at 350-360 nm, which is higher than of pure CuO nano sheet. The energy band gaps were 3.20 eV and 3.30 eV of CuO and CuO-CNR respectively. Finally antimicrobial activities of samples have been investigated against the Gram positive (pneumonia) and gram-negative (pseudomonas). The maximum antibacterial activities against the Gram positive (pneumonia) of CuO nano sheet and of CuO- cellulose nano rods are 16 mm and 19 mm respectively. The maximum antibacterial activities against the Gram negative (pseudomonas) of CuO nano sheet and of CuO- cellulose nano rods are 30 mm and 33 mm.
Article Type:
Research/Original Article
Language:
English
Published:
Journal of Nano Structures, Volume:9 Issue:4, 2019
Pages:
761 - 767
magiran.com/p2071118  
روش‌های دسترسی به متن این مطلب
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!