Studying on the fatigue behavior of Al- Al2O3 metal matrix nano composites processed through powder metallurgy
Message:
Abstract:
Excellent mechanical properties and fatigue performance of Al/Al2O3 metal-based nanocomposites caused to introduce this material as a good candidate for various applications. In this regard, the preparation and characterization of this composite can be considered as a hot issue for research. The study was carried out in several steps including: (i) preparation of Al/Al2O3 metal-based nanocomposites at various Al2O3 content as reinforcement (4, 6 and 8 wt.%) using wet attrition milling; (ii) hot forward extrusion process of prepared samples; (iii) determination of mechanical properties of prepared composite by tensile test; (iv) usage of rotating-bending fatigue test for determination of the fatigue performance of prepared composite and (v) analysis of the fracture surfaces of fatigue tests specimens to determine the mechanism/s of failure based on scanning electron microscope analysis. The results showed that the presence of Al2O3 nanoparticles up to 6 wt.% enhanced the fatigue strength of Al/Al2O3 nanocomposites while the higher amount of reinforcement has a detrimental effect on the fatigue strength. Also, the statistical nature of fatigue data confirmed the higher coherency as well as homogeneity of prepared composites by 6 wt.% of reinforcement. The EDX spectrum confirmed the presence of Al2O3 at the origin of crack. As a consequence, the most probable mechanisms for crack initiation through the cyclic loading can be considered as the fracture and/or detachment of reinforcement particles.
Article Type:
Research/Original Article
Language:
English
Published:
Journal of Ultrafine Grained and Nanostructured Materials, Volume:52 Issue:2, 2019
Pages:
210 - 217
magiran.com/p2072551  
روش‌های دسترسی به متن این مطلب
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!