The morphological and physico-mechanical properties of wood plastic composite made of polylactic acid polymer
Message:
Abstract:
This study aims to fabricate an eco-friendly wood plastic composite with poly (lactic acid) biodegradable matrix reinforced by wood flour and pulp fibers. Polylactic acid (PLA) samples were compared to the samples made from one of the most commonly used synthetic plastics, i.e. low density polyethylene to evaluate the results of this study. Besides, in order to achieve the best characteristics of the new composite, some effective factors such as the mixing percentage of the filler and matrix in four levels and the shape of the wood material in two levels of wood flour and pulp fibers were used as variables. Samples made of PLA and low density polyethylene were fabricated by flat press and by injection molding, respectively, according to ASTM standard. In this work, in addition to test the physical and mechanical properties, the morphological properties of the new product were studied by electron scanning microscopy. According to the results, the mechanical properties of all samples made of low density polyethylene and poly lactic acid increased with increasing content of paper fibers and wood flour and the highest mechanical strength was observed for samples containing low density polyethylene. The results of physical properties also showed that in all specimens, with a decrease in the content of wood flour and paper fibers, water absorption and thickness swelling were improved. In addition, samples made of low density polyethylene showed better physical properties than samples containing PLA polymer. Finally, by reviewing the results of this study and comparing the microscopic images of the samples, it can be concluded that the best mechanical and physical resistance are related to specimens made with low density polyethylene and wood flour.
Article Type:
Research/Original Article
Language:
Persian
Published:
Journal of Forest and Wood Products, Volume:72 Issue: 4, 2020
Pages:
339 - 349
magiran.com/p2092895  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
پرداخت با کارتهای اعتباری بین المللی از طریق PayPal امکانپذیر است.
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.