Experimental study and finite element simulation for determining the forming window of 6063-O aluminum tube in warm hydroforming process
Message:
Abstract:
In recent years, aluminum and magnesium alloys have attracted the attention of researchers and engineers due to higher strength to weight ratio, compared with steels. The main limitation of these alloys is the low formability at room temperature. In order to overcome this limitation, researchers have shown that the formability of aluminum alloys increases at high temperatures. Tube hydroforming is known as a novel metal forming process in which the fluid internal pressure and the axial force are applied simultaneously to the tube. In this study, the formability of 6063 annealed aluminum tube has been investigated in warm tube hydroforming process. The effects of pressure and axial feed on the thickness distribution, bursting pressure and the respecting bulge height at different temperatures have been studied experimentally and numerically. In order to numerically predict the onset of fracture in the process, three criteria, namely equivalent plastic strain acceleration (second derivative), major strain acceleration, and thickness strain acceleration were used. Moreover, a geometrical method was adopted in the simulation to determine the wrinkling. By comparing the results, there was an acceptable accordance between experimental and simulation results. By using experimental tests and finite element simulation, the process windows of the 6063 annealed aluminum tube were obtained at the temperature of 25 °C and 250 °C. According to the process window obtained at 25 °C compared with the one obtained at 250 °C, the pressure interval in the safe zone is about twice but the axial feed interval becomes nearly half.
Article Type:
Research/Original Article
Language:
Persian
Published:
Amirkabir Journal Mechanical Engineering, Volume:52 Issue: 3, 2020
Pages:
31 - 40
magiran.com/p2099963  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 300,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.