Experimental Study of Polyvinyl Acetate / Diamond Nanocomposites
Nanocomposites are a new class of materials that have at least one of their major constituents, at least in one dimension, in the range of one to one hundred nanometers. Typically, nanocomposites have different and superior properties in terms of mechanical and physical properties than conventional composites.
In this study, polyvinyl acetate was prepared by emulsion polymerization for polymer matrix. Then the diamond nanoparticles were modified with silane agent. Finally, polyvinyl acetate / diamond nanocomposite was prepared and analyzed with 0.5, 1, 1.5 and 2 wt% of modified diamond nanoparticles. To determine the properties and structure of the nanocomposite, FTIR, TGA, RMS, FESEM, oxygen permeation analysis was used in the films produced and contact angle measurements.
FTIR Analysis revealed that the modification of the diamond nanoparticles with the silane agent was well performed. FESEM images show that homogeneous nanocomposites were created. Oxygen permeability in polyvinyl acetate / diamond nanocomposite film decreases with increasing percentage of modified nanoparticles in nanocomposite. This is a valuable property if this nanocomposite is used as a fruit preservative coating. Contact angle measurement of polyvinyl acetate / diamond nanocomposite showed that by increasing the amount of modified diamond nanoparticles from 0.5 to 2 wt %, the hydrophobicity of nanocomposite film increased. Therefore, by increasing the specific amount of nanoparticles to the polymer matrix, the polymer properties such as heat resistance and tensile strength are increased which increases the efficiency of the polymer.
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.