Influence of Light-Curing Units on Color Stability of Composite Resins After Aging
Message:
Abstract:
Background and Aim

One of the most important problems with composite restorations is the loss of consistency between the composite and tooth color. The present study aimed to compare the color stability of two types of nanohybrid composites cured with different light-curing devices after aging.

Materials and Methods

In this study, the color stability of 40 disc-shaped specimens (10 mm in diameter and 2 mm in height) from two types of enamel and dentin nanohybrid composites (IPS Empress Direct, Ivoclar Vivadent) was investigated. A group of 10 samples of each composite was cured by light-emitting diode (LED) Bluephase device (Ivoclar, Vivadent) at 1200 mW/cm2 for 20 seconds, and another group of 10 specimens was cured by a quartz-tungsten-halogen (QTH) device (Coltolux 2.5, Colten, USA) at 600 mW/cm2 for 40 seconds. The initial color of the samples was determined by the Konica Minolta spectrophotometer (CS2000, USA), and then, the composite samples were subjected to an accelerated artificial aging (AAA) process in the QUV/SPRAY device. Then, the color of the samples was reassessed. Two-way analysis of variance (ANOVA) was used to compare the color changes in the study groups at a significance level of P=0.05.

Results

The specimens cured by the LED device showed significantly lower color change compared to QTH (P=0.047). However, there was no significant difference in color stability between enamel and dentin composites cured by a fixed apparatus (P=0.474).

Conclusion

The curing of nanohybrid composites with LED devices causes lower color change compared to QTH.

Article Type:
Research/Original Article
Language:
English
Published:
Journal of Research in Dental and Maxillofacial Sciences, Volume:5 Issue: 2, 2020
Pages:
21 - 25
magiran.com/p2139955  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.