Investigation on Failure Loads and Failure Modes for Two Parallel Pin-Loaded Holes Made from Unidirectional Glass-Epoxy Nanoclay Laminates
Message:
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:

Purpose of this study is to obtain failure modes and failure loads of two Parallel pin loaded holes in unidirectional glass fibre/epoxy by adding nanoclay in the absence of nanoclay composite laminates using finite element analysis; the results are validated through experiment. The geometrical parameters studies in this survey include the distance between the diameter of the hole (e/d) and the free edge of specimen, the distance between two holes-to-hole diameter (M/d). The samples were exposed to constant speed tensile loading. The results showed that by adding nanoclay, failure load increases and failure modes varies from shear out to bearing failure. Furthermore, increasing distance from the free edge of the pin centre’s increases load bearing capacity of two type of composite materials and changes the failure mode from shear to the bear, it increases and decreases the distance from canter’s of pin in layers with and without nanoclay particles, respectively and changes failure mode from shear to bear mode. In order to find morphology of specimens and dispersion quality, Scanning Electron Microscope (SEM) was used. For predicting failure load and differentiating failure modes, Tsai-hill failure criteria associated with material property degradation is used. Experimental and FEM results indicate importance of considering the impact of e/d and M/d ratios in the design of two Parallel pin joints. ANSYS was used to carry out numerical simulation and the results denote a good agreement between numerical and experimental results. In this study, by designing an experimental and numerical procedure to estimate the effect of nanoclay, on failure mode and failure load of typical composite material, glass-epoxy, we could illustrate that adding nanoclay brought with it improvement of shear and tensional strength of glass-epoxy about 10 %.

Language:
English
Published:
International Journal of Advanced Design and Manufacturing Technology, Volume:13 Issue: 2, Jun 2020
Pages:
119 to 127
magiran.com/p2152140  
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یک‌ساله به مبلغ 990,000ريال می‌توانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.
دسترسی سراسری کاربران دانشگاه پیام نور!
اعضای هیئت علمی و دانشجویان دانشگاه پیام نور در سراسر کشور، در صورت ثبت نام با ایمیل دانشگاهی، تا پایان فروردین ماه 1403 به مقالات سایت دسترسی خواهند داشت!
In order to view content subscription is required

Personal subscription
Subscribe magiran.com for 50 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!