Pulsed Nd: YAG laser dissimilar welding of Ti/Al3105 alloys
Author(s):
Article Type:
Research/Original Article (دارای رتبه معتبر)
Abstract:
Overlapped strips of titanium grade 2 and aluminum 3105-O alloy were welded together by an innovative spot-like pulse laser procedure. The tactile seam tracking on ring paths yielded reliable weld fit-up of 1 and 0.5 mm thickness strips. Since the welding parameters of Ti-Al were narrow, three welding speeds of 4, 5 and 6.67 mm•s-1 were chosen for the pretest conditions. The microstructural investigations showed that intermetallic compound Ti3Al, formed in Ti-rich fusion zone. Cracks formed in the Al-rich fusion zone as a result of TiAl3 precipitation. Dimple fracture occurred at 6.67 mm•s-1 welding speed. Longer mixing time at Ti-Al interface occurred at lower welding speeds of 4 and 5 mm•s-1, which led to the formation of thicker intermetallic compounds and more massive crack generation. It also increases the hardness of the fusion zone and results in brittle fracture type during the tensile test. The highest strength was achieved with a welding speed of 4 mm•s-1 which was a result of more massive weld nugget and lower porosity.
Language:
English
Published:
Scientia Iranica, Volume:27 Issue: 4, Jul Aug 2020
Pages:
1982 to 1994
magiran.com/p2163220
دانلود و مطالعه متن این مقاله با یکی از روشهای زیر امکان پذیر است:
اشتراک شخصی
با عضویت و پرداخت آنلاین حق اشتراک یکساله به مبلغ 1,390,000ريال میتوانید 70 عنوان مطلب دانلود کنید!
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی نامحدود همه کاربران به متن مطالب تهیه نمایند!
توجه!
- حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران میشود.
- پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانههای چاپی و دیجیتال را به کاربر نمیدهد.
In order to view content subscription is required
Personal subscription
Subscribe magiran.com for 70 € euros via PayPal and download 70 articles during a year.
Organization subscription
Please contact us to subscribe your university or library for unlimited access!