Effect of photo core, LuxaCore, and core max II core building materials on fracture resistance of endodontically‑treated teeth restored with fiber‑reinforced composite posts and ParaPosts
Message:
Abstract:
Background

Post and core treatment is commonly performed for endodontically treated teeth to replace the lost tooth structure and reinforce and protect the remaining dental tissue. This study aimed to compare the effect of three‑core building materials on fracture resistance of endodontically‑treated teeth restored with fiber‑reinforced composite (FRC) posts and ParaPosts.

Materials and Methods

This invitro, experimental study evaluated 108 sound, single‑rooted mandibular first premolars extracted for orthodontic purposes. The teeth were randomly divided into nine groups (n = 12) of control (no endodontic or restorative treatment), FRC + Photo Core (Group 2), FRC + LuxaCore (Group 3), FRC + Core Max II with bonding agent (Group 4), FRC + Core Max II without bonding agent (Group 5), ParaPost + Photo Core (Group 6), ParaPost + LuxaCore (Group 7), ParaPost + Core Max II with bonding agent (Group 8), and ParaPost + Core Max II without bonding agent (Group 9). The fracture resistance was measured by applying the load at 45° angle relative to the longitudinal axis of the tooth with a crosshead speed of 1 mm/min using a universal testing machine. Data were through descriptive statistics, Tukey’s test, and one‑way analysis of variance (α = 0.05).

Results

The mean fracture resistance was 454.0 ± 62.7, 410.8 ± 48.3, 365.1 ± 42.1, 423.7 ± 111.7, 392.4 ± 90.0, 292.3 ± 83.9, 242.3 ± 73.4, 278.2 ± 67.9, and 247.3 ± 49.6 N in Groups 1–9, respectively. Group 4 showed the highest fracture resistance, which was significantly higher than this study the value in all ParaPost and control groups (P < 0.05) but had no significant difference with the fracture resistance of other groups (P > 0.05).

Conclusion

Fracture resistance is independent of the type of core building material used, and the tested products had no superiority over each other. The mean fracture resistance of FRC post groups were significantly higher than that of ParaPost groups. Furthermore, Core Max II + bonding agent yielded insignificantly higher fracture resistance than Core Max II without bonding agent.

Article Type:
Research/Original Article
Language:
English
Published:
Dental Research Journal, Volume:17 Issue: 4, 2020
Pages:
244 - 250
magiran.com/p2169315  
برخی از خدمات از جمله دانلود متن مقالات تنها به مشترکان مگیران ارایه می‌گردد. شما می‌توانید به یکی از روش‌های زیر مشترک شوید:
اشتراک شخصی
در سایت عضو شوید و هزینه اشتراک یک‌ساله سایت به مبلغ 400,000ريال را پرداخت کنید. همزمان با برقراری دوره اشتراک بسته دانلود 100 مطلب نیز برای شما فعال خواهد شد!
پرداخت با کارتهای اعتباری بین المللی از طریق PayPal امکانپذیر است.
اشتراک سازمانی
به کتابخانه دانشگاه یا محل کار خود پیشنهاد کنید تا اشتراک سازمانی این پایگاه را برای دسترسی همه کاربران به متن مطالب خریداری نمایند!
توجه!
  • دسترسی به متن مقالات این پایگاه در قالب ارایه خدمات کتابخانه دیجیتال و با دریافت حق عضویت صورت می‌گیرد و مگیران بهایی برای هر مقاله تعیین نکرده و وجهی بابت آن دریافت نمی‌کند.
  • حق عضویت دریافتی صرف حمایت از نشریات عضو و نگهداری، تکمیل و توسعه مگیران می‌شود.
  • پرداخت حق اشتراک و دانلود مقالات اجازه بازنشر آن در سایر رسانه‌های چاپی و دیجیتال را به کاربر نمی‌دهد.